Minimum fretting amplitude in medium force for connector coated material and pure metals

E. Carvou
L. Tristani
  • Fonction : Auteur
E. M. Zindine
  • Fonction : Auteur

Résumé

For automotive applications, the mechanical behaviour of the contact area under vibrations is one of the key factors for connector reliability. Such vibrations are typically in the range of 10-2000Hz and result in displacements of only a few microns, at the contact interface. In the present study, a bench test has been developed to control more representative motions down to 1 mu m. The objective is to determine the minimum amplitude for fretting-corrosion degradation based on the evolution of contact resistance and to study the effects of the material, the contact force, the coating for these low displacement amplitudes. To obtain the limit of the appearance of fretting, a sub-micrometer incrementing displacement amplitude methodology was applied on high stiffness bench test including a double PZT actuator. It was found that the fretting degradation starts to occur from 2 mu m to 6 mu m when the contact force is from 0.5N to 2.5N with a tin coated terminal. Moreover pure copper, tin and nickel have similar amplitude fretting limits while noble metals confirm the absence of fretting up to
Fichier non déposé

Dates et versions

hal-01073297 , version 1 (09-10-2014)

Identifiants

  • HAL Id : hal-01073297 , version 1

Citer

A. Bouzera, E. Carvou, N. Ben Jemaa, R. El Abdi, L. Tristani, et al.. Minimum fretting amplitude in medium force for connector coated material and pure metals. Holm 2010, 2010, Charleston, United States. pp.101--107. ⟨hal-01073297⟩
68 Consultations
0 Téléchargements

Partager

Gmail Facebook X LinkedIn More