Magnetic Properties of Cobalt Films at the Initial Stage of Ion-Beam Deposition - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Pis'ma v Zhurnal Tekhnicheskoi Fiziki / Technical Physics Letters Année : 2009

Magnetic Properties of Cobalt Films at the Initial Stage of Ion-Beam Deposition

A. I. Stognij
  • Fonction : Auteur
V. F. Meshcheryakov
  • Fonction : Auteur
N. N. Novitskii
  • Fonction : Auteur
Farid Fettar
  • Fonction : Auteur
  • PersonId : 957737
M. V. Pashkevich
  • Fonction : Auteur

Résumé

Variations in the magnetic properties of ion-beam-deposited cobalt (Co) films from the onset of nucleation until the passage to a bulk-like state have been studied using ferromagnetic resonance (FMR) measurements at 9.55 GHz and SQUID magnetometry. Depending on the Co film thickness, the FMR line width ΔH exhibits a sharp transition from large values (0.24 kOe < ΔH < 0.33 kOe) at the initial deposition stage to slightly varying values of ΔH < 0.16 kOe for film thicknesses above 1 nm. Similarly, Co films with thicknesses below 1 nm exhibit a significant coercivity (HC > 0.54 kOe at 10 K), while thicker films are char acterized by HC < 0.16 kOe in the entire range of temperatures up to 300 K. Large values of ΔH and HC at the nucleation and initial growth stages are related to the contribution from a transition Co/Si layer formed under the action of self irradiation with a high-energy component of the deposited flux, which is inherent in the ion-beam sputtering in high vacuum. This fraction of high-energy Co atoms does not exceed 10% of their total flux and is characterized by a mean projected range of 0.8 nm in the growing Co layer and 1.2 nm in the Si substrate. Conditions of using Co films with intermediate thicknesses within 0.8 nm < t ≤ 2 nm for the injection of a spin-polarized current into silicon at room temperature are discussed.

Dates et versions

hal-01010771 , version 1 (20-06-2014)

Identifiants

Citer

A. I. Stognij, V. F. Meshcheryakov, N. N. Novitskii, Farid Fettar, M. V. Pashkevich. Magnetic Properties of Cobalt Films at the Initial Stage of Ion-Beam Deposition. Pis'ma v Zhurnal Tekhnicheskoi Fiziki / Technical Physics Letters, 2009, 35, pp.528. ⟨10.1134/S1063785009060145⟩. ⟨hal-01010771⟩