Composition and structural study of solution-processed Zn(S,O,OH) thin films grown using H2O2 based deposition route

Résumé

Recent results have revealed that the low deposition time issue of chemical bath deposited (CBD) Zn(S,O,OH) buffer layer used in Cu(In,Ga)Se-2 (CIGSe) solar cells could be resolved using H2O2 as an additive in the chemical bath solution. Although the use of this additive does not hinder the electrical properties of the resulting Zn(S,O,OH)-buffered CIGSe solar cells, the impact of H2O2 on the Zn(S,O,OH) properties remains unclear. The present contribution aims at determining the chemical composition and the microstructure of Zn(S,O,OH) film deposited by CBD using the alternative deposition bath containing the standard zinc sulfate, thiourea, ammonia but also H2O2 additive. Both X-ray photoemission spectroscopy and energy dispersive X-ray spectroscopy analyses reveal higher sulfur content in alternatively deposited Zn(S,O,OH), since the first step growth of the layer. According to transmission electron microscopy analyses, another consequence of the higher deposition rate achieved when adding H2O2 in the bath is the modification of the absorber/buffer interface. This could be explained by the enhancement of the cluster growth mechanism of the layer.

Dates et versions

hal-00961218 , version 1 (19-03-2014)

Identifiants

Citer

M. Buffiere, E. Gautron, T. Hildebrandt, Sylvie Harel, Catherine Guillot-Deudon, et al.. Composition and structural study of solution-processed Zn(S,O,OH) thin films grown using H2O2 based deposition route. Thin Solid Films, 2013, 535, pp.171. ⟨10.1016/j.tsf.2012.10.029⟩. ⟨hal-00961218⟩
130 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More