Tribological properties of hard a-C:H:F coatings

Résumé

Hydrogenated amorphous carbon thin films containing fluorine (a-C:H:F) have been produced by radiofrequency plasma enhanced chemical vapor deposition by using different F/H ratios in the gas phase. The introduction of fluorine from 0 to 19 at.% resulted in a decrease of hydrogen content and to the formation of C\F and C\F2 bonds. For all the films, Raman analysis showed a typical diamond-like carbon response with an evolution of the structure to larger sp2 clusters with less hydrogen while fluorine content increased. The drop in hardness generally observed in the literature with fluorine introduction was less abrupt here: for a fluorine content up to 6.5 at.%, the measured hardness was 28 GPa, and for 19 at.% of fluorine, value was 20 GPa. These are quite high values for a-C:H:F thin films. Moreover, fluorine improved tribological behavior in dry conditions with friction coefficient slightly reduced at low fluorine content and wear rate significantly reduced: divided by two to four than the fluorine free reference coating.

Dates et versions

hal-00918575 , version 1 (13-12-2013)

Identifiants

Citer

Cédric Jaoul, Christelle Dublanche-Tixier, O. Jarry, Pascal Tristant, J.P. Lavoute, et al.. Tribological properties of hard a-C:H:F coatings. Surface and Coatings Technology, 2013, 237, pp.28-332. ⟨10.1016/j.surfcoat.2013.07.042⟩. ⟨hal-00918575⟩
132 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More