Effects of Electron Beam Irradiation on Elasticity of CFRTP (CF/PEEK) - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Materials Transactions Année : 2011

Effects of Electron Beam Irradiation on Elasticity of CFRTP (CF/PEEK)

Résumé

Homogeneous low voltage electron beam irradiation (HLEBI) improved the elasticity indicated by both flexural modulus (E(f)) and the maximum slope value ((d sigma/d epsilon)(max)) of the bending stress strain curve of carbon fiber reinforced thermoplastic polyetheretherketone (CFRTP) composite sheets with 0.50 mm thickness, although the penetration depth estimated was from 0.14 to 0.21 mm on both side surfaces. HLEBI remarkably enhanced both E(f) and (d sigma/d epsilon)(max). The E(f) at middle cumulative probability (P(E)) of 0.50 for CFRTP irradiated at 0.30 MGy (kJg(-1)) was 3.3 GPa, which was 27% higher (2.6 GPa) than for CFRTP before irradiation. Moreover, (d sigma/d epsilon)(max) a at middle cumulative probability (P(E) = 0.50) was more than 4.9 GPa for CFRTP irradiated at 0.30 MGy. The interfacial friction force, as well as the strengthening of both carbon fiber and polyetheretherketone probably contributed to the HLEBI effects to enhance both E(f) and (d sigma/d epsilon)(max) in the CFRTP. [doi:10.2320/matertrans.MBW201005]

Dates et versions

hal-00851281 , version 1 (13-08-2013)

Identifiants

Citer

H. Takei, M. Salvia, Alain Vautrin. Effects of Electron Beam Irradiation on Elasticity of CFRTP (CF/PEEK). Materials Transactions, 2011, 52 (4), pp.734-739. ⟨10.2320/matertrans.MBW201005⟩. ⟨hal-00851281⟩
58 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More