Article Dans Une Revue Advances in Applied Ceramics Année : 2011

Phase transformation and sintering behaviour of mullite and mullite-zirconia composite materials

Résumé

Mullite is one of the most promising engineering materials for applications at elevated temperatures, but has poor mechanical properties at ambient temperature; therefore, it is usually reinforced with particles, fibres or whiskers to improve its properties. Among particles added to mullite are ZrO2 particles which improve its fracture toughness through the well known process of phase transformation from tetragonal to monoclinic in zirconia particles. The aim of the present work is to explore the utilisation of Algerian kaolin, alpha-Al2O3 and ZrO2 to synthesise mullite-ZrO2 composites through reaction sintering and investigate phase transformation and sintering behaviour of the composites. The raw materials were mixed through planetary ball milling followed by attrition milling. Compacted samples were sintered at temperatures between 1100 and 1600 degrees C for 2 h. The bulk density was measured by the water immersion method. X-ray diffraction (Rietveld method) was used to characterise phases present in the sintered samples. It was found that the zirconia phase retained its tetragonal structure with the addition of up to 16% zirconia. The formation of primary mullite in all samples was complete at 1250 degrees C. The cristobalite started to form at 1150 degrees C, and disappeared at 1300 degrees C in the samples of mullite, and at 1250 degrees C when ZrO2 was added. The zircon compound ZrSiO4 started to form at 1250 degrees C and completely disappeared at 1400 degrees C. The increase in ZrO2 ratio promoted the formation of grains with spherical shape.
Fichier non déposé

Dates et versions

hal-00851272 , version 1 (13-08-2013)

Identifiants

Citer

F. Sahnoune, Hocine Belhouchet, N. Saheb, Patrice Goeuriot. Phase transformation and sintering behaviour of mullite and mullite-zirconia composite materials. Advances in Applied Ceramics, 2011, 110 (3), pp.175-180. ⟨10.1179/1743676111Y.0000000004⟩. ⟨hal-00851272⟩

Collections

INSTITUT-TELECOM
39 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More