MnO2 Nanorods Prepared by Redox Reaction as Cathodes in Lithium Batteries
Résumé
α- and β-MnO2 phases have been synthesized by redox reaction of ammonium persulphate with manganese sulphate and manganese nitrate. A single phase of α-MnO2 was observed for the sample prepared from manganese sulphate, while β-MnO2 phase was obtained from manganese nitrate. Characteristic bands of hollandite and rutile phase were observed by FTIR. Nanorods structures were observed by images of transmission electron microscopy for both samples. Good electrochemical performance was observed for β-MnO2, which yields a specific discharge capacity of 180 and 130 mAh g−1 in the first and 45th cycle respectively. The specific discharge capacity of α-MnO2 is ca. 210 mAh g−1 at first cycle that decreases to 115 mAh g−1 in the 45th cycle.