The coexistence of two S (Al2CuMg) phases in Al-Cu-Mg alloys.

Résumé

The decomposition sequence of the supersaturated solid solution leading to the formation of the equilibrium S (Al2CuMg) phase in Al-Cu-Mg alloys has long been the subject of ambiguity and debate. This paper describes the identification of two distinct S phases with different lattice parameters, in a series of Al-2.5Cu-1.5Mg alloy samples, isothermally aged at temperatures between 200 and 400 degrees C for various times, using high-resolution synchrotron X-ray powder diffraction. The two S phases, denoted SI and S2, form in competition with one another, with SI being metastable with respect to S2. The lattice parameters of S2 are found to be in good agreement with those refined by Heying et al. (Z Naturforsch 2005;60B:491) for the equilibrium S phase. Despite the differences in their lattice parameters, both SI and S2 appear to have the crystal structure proposed by Perlitz and Westgren (Ark Kemi Min Geol 1943;16B:1). The lattice parameters of both SI and S2 are well defined, with little scatter between different samples treated for different times and temperatures, and there are no signs of the large range of lattice parameters reported by recent electron microscopy observations.

Domaines

Matériaux

Dates et versions

hal-00794215 , version 1 (25-02-2013)

Identifiants

Citer

M.J. Styles, C.R. Hutchinson, Y. Chen, A. Deschamps, T.J. Bastow. The coexistence of two S (Al2CuMg) phases in Al-Cu-Mg alloys.. Acta Materialia, 2012, 60 (20), pp.6940-6951. ⟨10.1016/j.actamat.2012.08.044⟩. ⟨hal-00794215⟩
109 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More