Magnetic Screening of NbN Multilayers Samples
Résumé
In 2006 Gurevich proposed to use nanoscale layers of superconducting materials with high values of Hc > Hc^Nb for magnetic shielding of bulk niobium to increase the breakdown magnetic field inside SC RF cavities [1]. We have deposited high quality "model" samples by magnetron sputtering on monocrystalline sapphire substrates. A 250 nm layer of niobium figures the bulk Nb. It was coated with a single and multi-stacks of NbN layers (25 or12 nm) separated by 15 nm MgO barriers, and characterized by X-Ray reflectivity and DC transport measurements. DC or AC measurement of HC1 is an important goal for multilayer evaluation during the sample evaluation phase. A clear increase of HC1 at low frequency is promising indication since HC1 is expected to increase with frequency (see e.g. [2] and references therein). We have measured the first penetration field (HP~HC1) on DC magnetization curves in a SQUID system. HP of NbN covered sample is increased compared to Nb alone. We have also developed a set-up that allows measuring a large range of field and temperature with a local probe method based on 3rd harmonic analysis. We have confirmed the screening behavior of a single 25 nm NbN layer placed on the top of a Nb Layer.
Fichier principal
TUIOA03.pdf (525.58 Ko)
Télécharger le fichier
TUIOA03_talk.ppt (5.83 Mo)
Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Format : Autre
Loading...