Precipitation and hardening behaviour of the Fe20Co18W alloy aged at 800 degrees C

Résumé

The hardness and the microstructure evolution are studied in the Fe20Co18W (mass %) alloy aged at 800 degrees C after a solution treatment at 1380 degrees C. The hardness strongly increases at the onset of the annealing treatment then decreases. The precipitation sequence is characterized using X-ray diffraction and transmission electron microscopy. Several phases are identified during the annealing: nanometric W rich clusters, FeCoW ordered domains, nanometric plate shaped precipitates of Laves phase then micrometric Laves phase precipitates. The specific effect of Co addition on mechanical properties of FeCoW alloys is likely due to the formation of the FeCoW ordered compound at the beginning of aging and to the larger stability domain of the Laves phase in these alloys.

Domaines

Matériaux

Dates et versions

hal-00632707 , version 1 (14-10-2011)

Identifiants

Citer

P. Galimberti, S. Lay, A. Antoni-Zdziobek, S. Coindeau, M. Veron, et al.. Precipitation and hardening behaviour of the Fe20Co18W alloy aged at 800 degrees C. Intermetallics, 2011, 19 (4), pp.556-562. ⟨10.1016/j.intermet.2010.12.007⟩. ⟨hal-00632707⟩
123 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More