An experimental study of thoriated tungsten cathodes operating at different current intensities in an atmospheric-pressure plasma torch
Résumé
Thoriated tungsten cathodes operating in an open-air plasma torch at current intensities between 30 and 200 A were experimentally studied. The morphology and composition of the cathode tip after arcing were investigated by scanning electron microscopy and energy-dispersive X-ray spectroscopy. Three relevant zones were found on the cathode tip (spot zone, thorium-depleted zone and thorium-enriched zone), and their dimensions were measured. For each current intensity, the spot temperature T during arcing was measured by one-colour pyrometry, and the spot current density was determined. Exponential growth was seen for the current density as the spot temperature increased. From the experimental data and the energy balance in the presheath, the dependence of the cathode effective work function ϕ on the arc current intensity and its dependence on T were determined. It was found that ϕ increased from ϕ = 2.64 eV when T ? 2900 K to ϕ = 3.06 eV when T ? 3700 K. These values are consistent with the presence in the spot of a layer of thorium atoms on the tungsten matrix during arcing. The atomic surface density of the layer determines the value of ϕ.
Fichier principal
PEER_stage2_10.1088%2F0022-3727%2F43%2F18%2F185204.pdf (1.24 Mo)
Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)