Grain size effect on electromechanical properties and non-linear response of dense nano and microstructured PIN-PT ceramics - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of the European Ceramic Society Année : 2010

Grain size effect on electromechanical properties and non-linear response of dense nano and microstructured PIN-PT ceramics

Résumé

Nanopowders of 0.63Pb(In1/2Nb1/2)O-3-0.37PbTiO(3) were synthesized by solid state reaction using the continuous attrition milling followed by high-energy ball milling techniques in air at room temperature. After milling for 8 h nanopowders of 20-30 nm grain size are obtained. Sintering by hot pressing of PIN-37PT green pellets leads to dense ceramics with average grain size varying from 100 nm to 1 mu m. The dielectric and piezoelectric properties of PIN-37PT nanostructured ceramics with grain size bigger than about 160 nm remain roughly unchanged and comparable to those of microstructured ceramics. In addition, the stability of the permittivity and dielectric losses under high ac electric field grows when the grain size decreases. The material becomes less non-linear with decreasing grain size. This result is attractive for acoustic transducer applications.

Dates et versions

hal-00583063 , version 1 (04-04-2011)

Identifiants

Citer

K. Alilat, M. P. Thi, H. Dammak, Christine Bogicevic, A. Albareda, et al.. Grain size effect on electromechanical properties and non-linear response of dense nano and microstructured PIN-PT ceramics. Journal of the European Ceramic Society, 2010, 30 (9), pp.1919-1924. ⟨10.1016/j.jeurceramsoc.2010.03.010⟩. ⟨hal-00583063⟩
58 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More