Effect of Asymmetric Rolling on Plastic Anisotropy of Low Carbon Steels during Simple Shear Tests

H.J. Kim
  • Fonction : Auteur
G. Vincze
  • Fonction : Auteur
F. Barlat
  • Fonction : Auteur
J.W. Yoon
  • Fonction : Auteur

Résumé

Simple shear tests are performed on low carbon steel pre-deformed in conventional, asymmetric and orthogonal-asymmetric rolling. The simple-shear tests were carried out at 0 degrees, 45 degrees and 135 degrees with respect to the previous rolling direction. For a reduction ratio of 15%, a transient stagnation in the hardening rate is observed at reloading for all changes in strain path. The shear stress level, the hardening rate and extent of the plateau appear to be insensitive to the preliminary applied rolling conditions. After a reduction ratio of 50%, plastic instability was detected at reloading for all the changes of strain path and rolling conditions studied. A specific heat treatment was then designed allowing the material to become ductile after rolling while retaining the fine microstructure and therefore the high strength. Promising results were obtained essentially for 45 degrees shear tests.
Fichier non déposé

Dates et versions

hal-00546173 , version 1 (13-12-2010)

Identifiants

  • HAL Id : hal-00546173 , version 1

Citer

J.J. Gracio, H.J. Kim, G. Vincze, B.B. Panigrahi, F. Barlat, et al.. Effect of Asymmetric Rolling on Plastic Anisotropy of Low Carbon Steels during Simple Shear Tests. 10th International Conference on Numerical Methods in Industrial Forming Processes (NUMIFORM 2010), Jun 2010, Pohang, South Korea. pp.181-184. ⟨hal-00546173⟩
67 Consultations
0 Téléchargements

Partager

Gmail Facebook X LinkedIn More