Dc-bias-field-induced Dielectric Relaxation and AC Conduction in CaCu3Ti4O12 Ceramics

Résumé

The dielectric relaxation and ac conduction of CaCu3Ti4O12 (CCTO) ceramics were investigated at different temperatures under a dc bias. The dc biases give rise to the space charges accumulating, namely electrode response, resulting in the significant increase of dielectric permittivity and dielectric loss tangent. Two Debey-like relaxations, arising from both electrode and grain boundary response, present in low frequency with the increase of the dc biases. The electrode relaxation and grain boundary relaxation are distinguished according to the impedance spectroscopy and the frequency dependent ac conductivity. The relaxation time of electrode and grain boundary is 0.955 ms and 0.026 ms with a dc bias of 10 V at 328 K, respectively.

Mots clés

Fichier principal
Vignette du fichier
PEER_stage2_10.1080%2F14786430801894551.pdf (1.13 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-00513860 , version 1 (01-09-2010)

Identifiants

Citer

Laijun Liu, Huiqing Fan, Lei Wang, Xiuli Chen, Pinyang Fang. Dc-bias-field-induced Dielectric Relaxation and AC Conduction in CaCu3Ti4O12 Ceramics. Philosophical Magazine, 2008, 88 (04), pp.537-545. ⟨10.1080/14786430801894551⟩. ⟨hal-00513860⟩
438 Consultations
303 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More