Nitrogen-substituted TiO2: investigation on the photocatalytic activity in the visible light range

Résumé

Nitrogen-doped titanium oxides are attractive materials for the degradation of organic pollutants in water due to their photocatalytic activity in the visible light range. The evolution of the photocatalytic properties was studied on a number of TiO x N y powder samples where x varied from 2 to 0 (TiO2 to TiN) through increasing the nitrogen content (y = 0-1). X-ray diffraction and Raman spectroscopy showed that an anatase type TiO x N y was obtained at low nitrogen contents (<2 wt%). With increasing nitrogen content a structural transition from anatase to cubic TiN was observed. Electron spin resonance measurements of the TiO x N y samples confirmed the presence of unpaired electrons and defects for the TiO x N y materials with low nitrogen content (<2 wt%). The photo-induced activity of the TiO x N y materials was evaluated under VIS illumination of solutions containing methylene blue as an organic probe. The TiO x N y samples exhibited an improved photocatalytic activity under visible light illumination compared to TiO2 at nitrogen levels lower than 2 wt%. A photocatalytic activity could not be detected at nitrogen levels higher than 10 wt% and after conversion of the TiO x N y into the cubic phase. Optimum photocatalytic activity in the visible range can be achieved at nitrogen levels lower than 2 wt% for TiO x N y materials.

Domaines

Matériaux

Dates et versions

hal-00497098 , version 1 (02-07-2010)

Identifiants

Citer

Franck Tessier, Cordt Zollfrank, Nahum Travitzky, Hans Windsheimer, Odile Merdrignac-Conanec, et al.. Nitrogen-substituted TiO2: investigation on the photocatalytic activity in the visible light range. Journal of Materials Science, 2009, 44 (22), pp.6110-6116. ⟨10.1007/s10853-009-3845-5⟩. ⟨hal-00497098⟩
170 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More