Elaboration and optimization of (Y,Er)Al3(BO3)4 glassy planar waveguides through the sol-gel process

Résumé

In this work, a sol-gel route was used to prepare Y0.9Er0.1Al3(BO3)4 glassy thin films by spin-coating technique looking for the preparation and optimization of planar waveguides for integrated optics. The films were deposited on silica and silicon substrates using stable sols synthesized by the sol-gel process. Deposits with thicknesses ranging between 520 and 720 nm were prepared by a multi-layer process involving heat treatments at different temperatures from glass transition to the film crystallization and using heating rates of 2 °C/min. The structural characterization of the layers was performed by using grazing incidence X-ray diffraction and Raman spectroscopy as a function of the heat treatment. Microstructural evolution in terms of annealing temperatures was followed by high resolution scanning electron microscopy and atomic force microscopy. Optical transmission spectra were used to determine the refractive index and the film thicknesses through the envelope method. The optical and guiding properties of the films were studied by m-line spectroscopy. The best films were monomode with 620 nm thickness and a refractive index around 1.664 at 980 nm wavelength. They showed good waveguiding properties with high light-coupling efficiency and low propagation loss at 632.8 and 1550 nm of about 0.88 dB/cm.

Dates et versions

hal-00496690 , version 1 (01-07-2010)

Identifiants

Citer

Lauro J. Q. Maia, Jochen Fick, Christophe Bouchard, Valmor R. Mastelaro, Antonio Carlos Hernandes, et al.. Elaboration and optimization of (Y,Er)Al3(BO3)4 glassy planar waveguides through the sol-gel process. Optical Materials, 2009, 32, pp.484. ⟨10.1016/j.optmat.2009.10.008⟩. ⟨hal-00496690⟩

Collections

UGA CNRS NEEL
74 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More