Electrokinetic characterization of the Al2O3 ceramic MF membrane by streaming potential measurements

Je. Zhou
  • Fonction : Auteur
Xz. Zhang
  • Fonction : Auteur
Yq. Wang
  • Fonction : Auteur
Xb. Hu
  • Fonction : Auteur
Andre Larbot
  • Fonction : Auteur
  • PersonId : 863962
Michel Persin
  • Fonction : Auteur
  • PersonId : 863963

Résumé

The alumina microfiltration(MF) membrane was modified with nanocrystalline TiO2 in the pore wall. The electrokinetic properties of unmodified and modified alumina membranes were characterized by streaming potential measurements during tangential filtration at various conditions of pH, ionic concentration and ionic species in solutions. The modified membrane reveals a more acidic characteristic. The influence of pH value on the streaming potential of both membranes is explained by the shifting of the proton equilibrium that occurs at the surface of the membrane. The modification of the alumina membrane with TiO2 leads to the decrease of its isoelectric point (IEP) from 6.1 to 4.0 when filtered with NaCl solution. The ionic concentration and electrolyte species also have influence on the streaming potential of both membranes. The reversal of the streaming potential sign and the change of the isoelectric point of the membrane when filtered with CaCl2 and Na2SO4 solutions show specific adsorption of Ca2+ and SO42- ions onto the surface

Dates et versions

hal-00424246 , version 1 (14-10-2009)

Identifiants

Citer

Je. Zhou, Xz. Zhang, Yq. Wang, Xb. Hu, Andre Larbot, et al.. Electrokinetic characterization of the Al2O3 ceramic MF membrane by streaming potential measurements. Desalination, 2009, 235 (1 - 3), pp.102 - 109. ⟨10.1016/j.desal.2008.01.013⟩. ⟨hal-00424246⟩
69 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More