Metal organic vapour phase epitaxial growth of indium-rich InGaN alloys with robust photoluminescence properties

Matthieu Moret
Sandra Ruffenach
  • Fonction : Auteur
  • PersonId : 860798
Olivier Briot
B. Gil

Résumé

We report the growth of indium-rich InGaN alloys by metal-organic vapour phase epitaxy, using ammonia, trimethylgallium and trimethylindium as precursors. Compared to indium nitride, our alloy samples present substantial photoluminescence robustness with temperature. The analysis of the optical properties of these samples versus temperature indicates the existence of two non radiative recombination channels: one with a thermal activation temperature of 77 K and another one with an activation temperature ranging from 300 K for InN up to 640 K for In0.72Ga0.28N. The latter competes with the former at low temperatures whilst the former rules the optical properties at ambient conditions
Fichier non déposé

Dates et versions

hal-00390126 , version 1 (01-06-2009)

Identifiants

  • HAL Id : hal-00390126 , version 1

Citer

Matthieu Moret, Sandra Ruffenach, Olivier Briot, B. Gil. Metal organic vapour phase epitaxial growth of indium-rich InGaN alloys with robust photoluminescence properties. European Physical Journal: Applied Physics, 2009, 45 (2), pp.20305. ⟨hal-00390126⟩
9 Consultations
0 Téléchargements

Partager

Gmail Facebook X LinkedIn More