Non-equilibrium nitrogen DC-arc plasma treatment of TiO2 nanopowder

Résumé

Non-equilibrium nitrogen DC-arc plasma treatment of a commercial TiO2 anatase nanopowder was examined to obtain nitrogen-doped TiO2. By using a non-thermal discharge at low current (150 mA) and high voltage (1200 V) using pure N2 gas, light yellowish-gray TiO2 powder was successfully obtained within a short period of 5-10 min. XPS and TEM-EELS studies confirmed the existence of doped nitrogen. Due to the relatively mild conditions (plasma power of 180 W), metastable anatase structure and fine crystallite size of TiO2 (ca. 10 nm) were maintained after the plasma treatment. The in-flight powder treatment system used in this study is promising for various type of powder treatment
Fichier non déposé

Dates et versions

hal-00359177 , version 1 (06-02-2009)

Identifiants

Citer

Yoshikazu Suzuki, José Gonzalez-Aguilar, Noel Traisnel, Marie-Hélène Berger, Monique Repoux, et al.. Non-equilibrium nitrogen DC-arc plasma treatment of TiO2 nanopowder. Journal of Nanoscience and Nanotechnology, 2009, 9, pp.Pages 256-260. ⟨10.1166/jnn.2009.J035⟩. ⟨hal-00359177⟩
96 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More