Synthesis of a red iron oxide/montmorillonite pigment in a CO2-rich brine solution

German Montes Hernandez
Connectez-vous pour contacter l'auteur
Frederic Villieras

Résumé

The homoionic calcium-montmorillonite was used to synthesize a red iron oxide/clay pigment in a CO2-rich brine solution (0.5 M of NaCl) by using an agitated batch-reactor (engineer autoclave). The operating conditions were 15 days of reaction, 200 bars of pressure and 150 °C of temperature. SEM/EDS, STEM/EDS, XRD and Infrared Spectrometry were performed to characterize before and after reaction the solid phase. The results showed the precipitation of spherical nanoparticles (50–500 nm) of iron oxide (Fe2O3) dispersed and/or coagulated in the clay-matrix. Evidently, this oxide produced red coloration in the final product. For this case, the Fe3+ cation was provided to the aqueous solution by the dissolution of Ca-montmorillonite, particularly, the dissolution of most fine particles contained in the starting clay material. The cation exchange process and precipitation of polymorph silica were also observed.
Fichier principal
Vignette du fichier
Synthesis_of_a_red_iron_oxide.pdf (566.52 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-00202497 , version 1 (07-01-2008)

Identifiants

Citer

German Montes Hernandez, Jacques Pironon, Frederic Villieras. Synthesis of a red iron oxide/montmorillonite pigment in a CO2-rich brine solution. Journal of Colloid and Interface Science, 2006, 303, pp.472-476. ⟨10.1016/j.jcis.2006.07.064⟩. ⟨hal-00202497⟩

Collections

CNRS UNIV-LORRAINE
105 Consultations
1065 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More