FePt films on self-assembled SiO2 particle arrays

D. Makarov
  • Fonction : Auteur
C. Brombacher
  • Fonction : Auteur
M. Parlinska
  • Fonction : Auteur
S. Meier
  • Fonction : Auteur
P. Kappenberger
  • Fonction : Auteur
M. Albrecht
  • Fonction : Auteur

Résumé

Chemically L10 ordered (001) textured FePt thin films with perpendicular magnetic anisotropy can be grown on amorphous planar SiO2 substrate with an underlayer stack of [Pt (3nm)∕Cr (50nm)] adopting a [002] orientation when deposited at 350°C. This knowledge of optimum layer stack was transferred to self-assembled SiO2 particle arrays. While 330nm SiO2 particle arrays reveal perpendicular magnetic anisotropy with a remanence of almost one and a coercivity of 370mT, on 160nm particles, the FePt caps show a (111) texturing, leading to the random orientation of the easy axis of the magnetization.

Dates et versions

hal-00196201 , version 1 (12-12-2007)

Licence

Paternité

Identifiants

Citer

D. Makarov, C. Brombacher, F. Liscio, M. Maret, M. Parlinska, et al.. FePt films on self-assembled SiO2 particle arrays. Journal of Applied Physics, 2008, 103, ⟨10.1063/1.2841729⟩. ⟨hal-00196201⟩

Collections

UGA CNRS SIMAP
545 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More