Manganese Dioxides Surface Properties Studied by XPS and Gas Adsorption

Résumé

Structurally well defined g-MnO2 in terms of Pr and Tw were studied using X-ray photoelectron spectroscopy ~XPS! to complete surface investigations performed by high-resolution gas adsorption, water adsorption, and acid-base surface titration. The O 1s and Mn 2p spectra were deconvoluted into three components Mn-OH2 1 , Mn-OH, and Mn-O2. Analysis of the O 1s spectra in energy shift and relative intensity shows that 70 to 80% of the surface groups stay as neutral OH, 5% as Mn-OH2 and 20 to 30% as Mn-OH: their relative amount varies with Pr as well as PZC, water cross-sectional area and energetic constant C. Mn 2p spectra are far less sensitive than O 1s to the charge variation. Nevertheless a correlation is shown between the relative amount of surface species, the binding energy of Mn 5 O and O 5 Mn species and Tw.
Fichier non déposé

Dates et versions

hal-00110226 , version 1 (26-10-2006)

Identifiants

Citer

Bénédicte Prélot, Christiane Poinsignon, Grégory Berthomé, Fabien Thomas, Frédéric Villiéras. Manganese Dioxides Surface Properties Studied by XPS and Gas Adsorption. Journal of The Electrochemical Society, 2004, 151, pp.A1611. ⟨10.1149/1.1789411⟩. ⟨hal-00110226⟩
86 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More