Growth and characterization of InAs quantum dots on GaAs (100) emitting at 1.31μm

Résumé

ABSTRACT Self-organized InAs quantum dots (QDs) were grown in the Stranski-Krastanov regime, by gas-source molecular beam epitaxy (GSMBE), on (100) GaAs substrates. Two important parameters have been optimized in order to grow high quality QDs with a very good reproducibility: InAs growth rate and GaAs cap layer deposition rate. Atomic force microscopy (AFM) analysis shows a unimodal QD distribution and the room temperature photoluminescence (RTPL) spectrum of the optimized sample reveals a 1.3 μm emission with a 19 meV full width at half maximum (FWHM). Photoluminescence (PL) measurements versus excitation power density and photoluminescence excitation (PLE) measurements clearly show multi-component PL emission from transitions associated with fundamental and related excited states of QDs. Furthermore a good growth reproducibility is observed. The results are promising for further work which will lead to laser fabrication.
Fichier principal
Vignette du fichier
celibert2003.pdf (176.35 Ko) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-02353320 , version 1 (16-04-2024)

Identifiants

Citer

Vincent Célibert, Bassem Salem, Gérard Guillot, Catherine Bru-Chevallier, Laurent Grenouillet, et al.. Growth and characterization of InAs quantum dots on GaAs (100) emitting at 1.31μm. MRS Online Proceedings Library, 2003, Materials Research Society Symposium - Proceedings, 794, pp. 207-212. ⟨10.1557/PROC-799-Z7.8/T7.8⟩. ⟨hal-02353320⟩
47 Consultations
2 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More