Chemical reactivity between sol–gel deposited Pb(Zr,Ti)O$_3$ layers and their GaAs substrates

Résumé

We show how chemical interactions between the growing material and the substrate affect the crystallization of Pb(Zr,Ti)O$_3$ (PZT) thin films on SrTiO$_3$-templated GaAs substrates. A liquid PZT precursor (sol) is spin-coated on STO/GaAs pseudo-substrates grown by molecular beam epitaxy and crystallized by annealing under air. Complete crystallization of the PZT layers cannot be achieved due to significant oxidation of the GaAs substrate which enhances As diffusion through the structure and further formation of parasitic compounds containing Pb, Sr and As due to the strong chemical affinity between As anions and Pb and Sr cations. These mechanisms are extensively studied based on X-ray diffraction measurements carried out in situ during annealing and on transmission electron microscopy experiments including energy-dispersive X-ray analyses.
Fichier principal
Vignette du fichier
meunier2016.pdf (498.87 Ko) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-01489114 , version 1 (28-05-2024)

Identifiants

Citer

Benjamin Meunier, Ludovic Largeau, Philippe Regreny, Jose Penuelas, Romain Bachelet, et al.. Chemical reactivity between sol–gel deposited Pb(Zr,Ti)O$_3$ layers and their GaAs substrates. CrystEngComm, 2016, 18 (39), pp.7494. ⟨10.1039/C6CE01276K⟩. ⟨hal-01489114⟩
339 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More