Initiation and propagation of rebar corrosion in carbonated and cracked concrete
Identification des phases d'initiation et de propagation de la corrosion des armatures enrobées dans un béton fissuré et carbonaté
Résumé
Rebar corrosion is the major threat for the durability of reinforced concrete structures. In the case of the cooling towers of nuclear power plants, corrosion is induced by the carbonation of the concrete cover. In the presence of cracks carbonation can be significantly accelerated at the vicinity
of the cracks. It is therefore of first importance to characterize the impact of cracks on the initiation and propagation of rebar corrosion. It was the objective of the Ph.D. thesis. A large experimental campaign was set up and specific attention was paid to the test protocols so that the tests were
representative of the cooling towers service conditions.
La corrosion des aciers de renforcement constitue la principale pathologie des ouvrages en béton armé. Dans le cas des tours aéroréfrigérantes des centrales nucléaires d’EDF, elle est déclenchée par la carbonatation de l’enrobage en béton. La présence de fissures sur les parements des
ouvrages peut conduire à une carbonatation plus rapide au voisinage des fissures. Il est donc important de caractériser l’impact de ces fissures sur l’initiation voire la propagation de la corrosion des armatures. Une large campagne expérimentale a été mise en place dans le cadre de cette thèse et
une attention a été portée aux protocoles expérimentaux dans le but de se rapprocher des conditions de service des tours aéroréfrigérantes.