Article Dans Une Revue Materials Science Forum Année : 2010

Mechanical behavior study of plasma sprayed hydroxyapatite coatings onto Ti6Al4V substrates using scratch test

Résumé

Mechanical behavior and fracture mechanisms of plasma sprayed hydroxyapatite coatings on Ti-6Al-4V substrate were assessed taking into consideration two variables: the coating thickness and the substrate roughness. The results show that the specimens having a substrate arithmetic average roughness parameter Ra = 2.29 μm is favorable with respect to Ra = 1.23 μm. For coating thickness above 105 μm, cracks can be observed in the coating/substrate interface and the higher critical load Pc2 (used generally in comparative evaluation of adherence) decreases. A 90 μm coating thickness sprayed on a substrate having an arithmetic average roughness parameter Ra equal to 2.29 μm seems to be the best compromise between microstructure, mechanical resistance (high critical loads and fairly good contact quality) and long term stability in the physiological medium (low dissolution rate) for an orthopedic application.

Fichier principal
Vignette du fichier
LMPGM_MSF_2010_IOST.pdf (1.89 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Licence

Dates et versions

hal-05019278 , version 1 (03-04-2025)

Licence

Identifiants

Citer

Aliasghar Behnamghader, D. Najjar, Alain Iost, Stéphane Benayoun. Mechanical behavior study of plasma sprayed hydroxyapatite coatings onto Ti6Al4V substrates using scratch test. Materials Science Forum, 2010, 638-642, pp.641-646. ⟨10.4028/www.scientific.net/MSF.638-642.641⟩. ⟨hal-05019278⟩
30 Consultations
59 Téléchargements

Altmetric

Partager

  • More