Adhesion at poly(butylacrylate)-poly(dimethylsiloxane) interfaces

Résumé

We present an investigation of the adhesion modulation mechanisms of silica-like nanoparticles (MQ resins) incorporated in polydimethylsiloxane (PDMS) elastomers and acrylic adhesives. The Johnson-Kendall-Roberts (JKR) test has been used to gain information on the both zero velocity and the velocity dependence of the adhesive strength, avoiding as much as possible contributions to the adhesive strength of bulk dissipation in the adhesive (which is not the case with peel tests). As the incorporation of the MQ resins into the elastomers deeply affects their own mechanical properties, the loading and unloading curves of small poly(butylacrylate) (PBA) lenses on either PDMS elastomers, adsorbed PDMS and pure MQ resin layers are compared in a systematic manner. The PBA chains are observed to have a neat affinity for the MQ resin nanoparticles. When MQ resins are present at the interface, they tend to prevent facture propagation, thus producing a larger deformation of the PBA lens. The modulation of adhesion is then dominated by the corresponding dissipation inside the acrylic adhesive.

Fichier non déposé

Dates et versions

hal-04896923 , version 1 (20-01-2025)

Identifiants

Citer

Nicolas Amouroux, Frédéric Restagno, Liliane Léger. Adhesion at poly(butylacrylate)-poly(dimethylsiloxane) interfaces. The Journal of Adhesion, 2007, 83 (8), pp.741-760. ⟨10.1080/00218460701585840⟩. ⟨hal-04896923⟩
48 Consultations
0 Téléchargements

Altmetric

Partager

  • More