Dielectric and structural properties of diffuse ferroelectric phase transition in Pb 1.85 K 1.15 Li 0.15 Nb 5 O 15 ceramic
Résumé
We studied the structural and dielectric properties of new Tetragonal Tungsten Bronze (TTB) ceramics Pb1.85K1.15Li0.15Nb5O15 that was synthesized by solid-state reaction. We pay a special attention to the diffuse phase transition (DPT) that occurs close to 425 °C. Using dielectric measurements in a frequency range of 10 Hz–1 MHz and in the temperature range 30–560 °C, we have shown that the real permittivity close to DPT is well described by Santos-Eiras phenomenological model. Space-charge polarization, relaxation phenomena and free charges conductivity have been analyzed using dielectric spectroscopy impedance and modulus characterization. Cole-Cole plots show a non-Debye (polydispersive) type relaxation. In paraelectric phase the Arrhenius activation energy was determined as Eτ = 0.72 eV. We demonstrated that frequency dependence of ac conductivity at different temperatures obeys the Jonscher's universal law: σac = σdc + A(ω)n.