Tribochemistry dependence of Ni62Nb33Zr5 bulk metallic glass on the Cr content of steel counterparts
Résumé
Recent literature showed that Bulk Metallic Glasses can demonstrate repeatable tribological response, and that it might be controlled through a careful selection of the sliding counterpart’s composition. The present study focuses on the effect of Cr content of a steel ball sliding over a Ni62Nb33Zr5 BMG. Three different steels were chosen (C90, 100Cr6, and X105CrMo17) because they demonstrate similar constitutive elements, similar mechanical properties, but different Cr contents. Increasing Cr content resulted in an increase of friction coefficient from 0.13 to 0.85 while maintaining extremely low wear. In depth chemical analysis showed that increasing Cr content favors the loss of the ductile Nb2O5 of protective FeNbO4, and NiNb-oxide to the benefit of NiCrO, CrNbO4, NiFe-oxides, and Cr(VI) oxide.
Domaines
Matériaux
Fichier principal
ORIGINAL_FILE_Tribology International 198_2024_109923.pdf (1.55 Mo)
Télécharger le fichier
| Origine | Fichiers produits par l'(les) auteur(s) |
|---|