Effect of supercritical carbonation on porous structure and mechanical strength of cementitious materials modified with bacterial nanocellulose - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Materials and structures Année : 2023

Effect of supercritical carbonation on porous structure and mechanical strength of cementitious materials modified with bacterial nanocellulose

Résumé

The effect of wet supercritical CO2 (90 °C and 20 MPa) on the performance of cement paste (PC) modified with bacterial nanocellulose (BNC) was investigated. The pore structure of carbonated cement shows a clogging over the outer rim of the samples. In contrast, near the sample core, the characteristic peak of pore size distribution shifted towards smaller pores analyzed by mercury intrusion porosimetry. The effect of the carbonation overtime on mechanical properties shows increasing alteration. XRD results show more crystalline phases of hydrated cement in the BNC samples before carbonation. Cement reinforced with BNC shows lower density, a reduction in its porosity, and experiences fewer porosity changes at the cement core. Furthermore, its mechanical performance was less affected by the carbonation process.
Fichier sous embargo
Fichier sous embargo
0 0 10
Année Mois Jours
Avant la publication
mercredi 15 mai 2024
Fichier sous embargo
mercredi 15 mai 2024
Connectez-vous pour demander l'accès au fichier

Dates et versions

hal-04393067 , version 1 (14-01-2024)

Licence

Paternité

Identifiants

Citer

Juan Cruz Barría, Diego Manzanal, Siavash Ghabezloo, Jean-Michel Pereira. Effect of supercritical carbonation on porous structure and mechanical strength of cementitious materials modified with bacterial nanocellulose. Materials and structures, 2023, 56 (10), pp.180. ⟨10.1617/s11527-023-02264-z⟩. ⟨hal-04393067⟩
18 Consultations
1 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More