Optically selective SiC-based nanocomposite objects derived from titanium and boron-modified polycarbosilanes - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Open Ceramics Année : 2023

Optically selective SiC-based nanocomposite objects derived from titanium and boron-modified polycarbosilanes

Maxime Balestrat
Maxime Cheype
  • Fonction : Auteur
Pierre Carles
  • Fonction : Auteur
Xavier Deschanels
  • Fonction : Auteur
Audrey Soum-Glaude
Fabrice Rossignol
  • Fonction : Auteur
Nicolas Pradeilles

Résumé

Herein, we introduce a bottom-up material design approach of optically selective SiC-based nanocomposite objects. Precursors have been firstly synthesized by reaction of allylhydridopolycarbosilane with titanium and boron complexes before a pyrolysis at 1000 °C in flowing argon to deliver single-phase amorphous Si–Ti–C–N(B,H) ceramics. The later was then heat-treated up to 1800 °C under argon. Relatively dense nanocomposites made of TiCxN1-x (0 ≤ x ≤ 1) nanocrystals homogeneously formed in situ in a SiCxN4-x-type phases (0 ≤ x ≤ 4) have been isolated after heat-treatment at 1400 °C. Above 1400 °C, our experimental data showed a continuous evolution of carbon and nitrogen contents up to 1800 °C due to carbothermal reduction reactions forming carbide phases while releasing nitrogen-containing species. Thus, heat-treatment at 1800 °C led to porous and fully crystallized TiC(N)/SiC(B) nanocomposites that displayed a maximal optical selectivity of 1.67 measured at room temperature; a value significantly increased compared to the SiC(B) counterpart.

Mots clés

Domaines

Chimie
Fichier principal
Vignette du fichier
1-s2.0-S2666539523000251-main.pdf (8.64 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-04296320 , version 1 (20-11-2023)

Identifiants

Citer

Maxime Balestrat, Maxime Cheype, Pierre Carles, Xavier Deschanels, Audrey Soum-Glaude, et al.. Optically selective SiC-based nanocomposite objects derived from titanium and boron-modified polycarbosilanes. Open Ceramics, 2023, 14, pp.100353. ⟨10.1016/j.oceram.2023.100353⟩. ⟨hal-04296320⟩
21 Consultations
9 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More