Development of biomass‐based slurry for the manufacture of furan/cellulose composite by cast molding and 3D printing - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Polymer Science Année : 2023

Development of biomass‐based slurry for the manufacture of furan/cellulose composite by cast molding and 3D printing

Résumé

This study aims to develop a green composite based on two biomass‐based components via the curing of an oligomeric furfuryl resin coupled with 18–31 wt% cellulose powder. The curing was performed in an atmospheric pressure open air oven. The chemical composition of the used pre‐polymer was characterized with Fourier transform infrared and NMR spectroscopy and its curing reaction was followed by differential scanning calorimetry. The final cured composites were characterized to investigate the effect of cellulose addition on their morphology, dimensional stability, and thermo‐mechanical performances. The manufactured composite showed good thermal stability up to 200°C with a storage modulus higher than 2 GPa, and a mass loss under 3%. Moreover, the filler improved the composite dimensional stability upon crosslinking by 38% and the mechanical performances with respectively 15% and 40% increase in the Young's and flexural moduli. By the same token, cellulose prevented the typical foaming of poly(furfuryl alcohol) resins crosslinked at high temperature and low pressure. Preliminary tests highlighted the excellent processability of the developed composite, which was used to manufacture a static demonstrator coupling different fabrication techniques, that is, 3D printing (direct ink writing), high temperature compression molding and CNC machining.
Fichier principal
Vignette du fichier
MS JAPS - revised.pdf (1.66 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04294585 , version 1 (20-11-2023)

Identifiants

Citer

Khaoula Bouzidi, Didier Chaussy, Alessandro Gandini, Roberta Bongiovanni, Davide Beneventi. Development of biomass‐based slurry for the manufacture of furan/cellulose composite by cast molding and 3D printing. Journal of Polymer Science, 2023, 61 (17), pp.2060-2075. ⟨10.1002/pol.20230074⟩. ⟨hal-04294585⟩

Collections

UGA CNRS LGP2
18 Consultations
59 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More