Of Glasses and Crystals: Mitigating the Deactivation of CaO-Based CO2 Sorbents through Calcium Aluminosilicates
Abstract
CaO-based sorbents are cost-efficient materials for high temperature CO2 capture, yet they rapidly deactivate over carbonation-regeneration cycles due to sintering, hindering their utilization at industrial scale. Morphological stabilizers such as Al2O3 or SiO2 (e.g. introduced via impregnation) can improve sintering-resistance, but the sorbents still deactivate through the formation of mixed oxide phases and phase segregation, rendering the stabilization inefficient. Here, we introduce a strategy to mitigate these deactivation mechanisms by applying glassy (Al,Si)Ox overcoats via atomic layer deposition onto CaCO3 nanoparticles and benchmark the CO2 uptake of the resulting sorbent against sorbents with optimized overcoats of only alumina/silica (+ 25 %) and unstabilized CaCO3 nanoparticles (+ 55 %). 27 Al and 29 Si NMR studies reveal that the improved CO2 uptake and structural stability of sorbents with (Al,Si)Ox overcoats is linked to the formation of glassy calcium aluminosilicate phases (Ca,Al,Si)Ox that prevent sintering and phase segregation, probably due to a slower self-diffusion of cations in the glassy phases, reducing in turn the formation of CO2 capture-inactive Ca-containing mixed oxides. This strategy provides a roadmap for the design of more efficient CaO-based sorbents using glassy stabilizers.
Domains
Chemical Sciences
Fichier principal
ALD_NMR_JACS_Au_Manuscript.pdf (871.04 Ko)
Télécharger le fichier
ALD_NMR_JACS_Au_SI.pdf (1.38 Mo)
Télécharger le fichier
Origin : Files produced by the author(s)
Origin : Files produced by the author(s)