High-Responsivity Planar Photodetector Based on Methylammonium Lead Bromide Perovskite Thin Film

Pavlo Mai
  • Fonction : Auteur
Julien Houel
Benoit Mahler

Résumé

We have fabricated planar interdigitated photodetectors exhibiting high responsivity. These detectors are based on thin layers of methylammonium lead bromide (MAPbBr3) at 90 nm thickness. MAPbBr3 thin films were first characterized on glass (borosilicate) substrates using absorption and photoluminescence measurements showing a high absorption edge at 521 nm and strong emission at 530 nm, as expected. MAPbBr3 thin films were then deposited on top of interdigitated electrodes, hence producing planar photodetectors with responsivity up to 0.4 A/W. Such higher performances were attributed to the interdigitated design, low crack density (0.05 µm−2), and lower resistivity (20 MΩ.cm) compared to MAPbBr3 single crystal. Therefore, this work highlights MAPbBr3 thin films as very promising for photodetection applications.
Fichier principal
Vignette du fichier
photonics-10-01043.pdf (1.45 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte
Licence : CC BY - Paternité

Dates et versions

hal-04267826 , version 1 (02-11-2023)

Identifiants

Citer

Pavlo Mai, Julien Houel, Nathan Dreveton, Benoit Mahler, Alban Gassenq. High-Responsivity Planar Photodetector Based on Methylammonium Lead Bromide Perovskite Thin Film. Photonics, 2023, 10 (9), pp.1043. ⟨10.3390/photonics10091043⟩. ⟨hal-04267826⟩
18 Consultations
13 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More