Room-Temperature Sintering of Amorphous Thiophosphate Solid Electrolyte (Li 3 PS 4 ): Coupling Morphological Evolution to Electrochemical Properties - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Advanced Functional Materials Année : 2024

Room-Temperature Sintering of Amorphous Thiophosphate Solid Electrolyte (Li 3 PS 4 ): Coupling Morphological Evolution to Electrochemical Properties

Résumé

Thiophosphate solid electrolytes (Li 3 PS 4 , hereafter denoted LPS) have the advantage of presenting a reasonable ionic conductivity at room temperature (≈ 0.3 mS cm −1) and an easy manufacturing, meaning that they can be sintered at room temperature. Unfortunately, during cycling, several chemo-mechanical degradations quite often attributed to the electrochemical activities occur, but they could also be linked to the sintering process. To date, a fundamental understanding of room-temperature sintering and its impact on the microstructure, the ionic conductivity, and the link between electrochemistry and structure/morphology remains imprecise. In this study, a comprehensive study of homemade amorphous 75% Li 2 S-25% P 2 S 5 (Li 3 PS 4) is presented, investigating the influence of pressure and time of room temperature sintering. Focused ion beam-scanning electron microscopy coupled to electrochemical techniques such as electrochemical impedance spectroscopy, Li plating/ stripping and coupled to structural techniques such as wide-angle X-ray scattering are used to establish the link between structure, morphology, and electrochemical properties. It is demonstrated that the room temperature sintering of solid electrolytes is not that trivial and that the commonly accepted rule "less porosity = better ionic conductivity" is not always true and that many additional parameters should be considered to properly sinter the solid electrolyte.
Fichier principal
Vignette du fichier
Papier_LPS.pdf (3.57 Mo) Télécharger le fichier
Origine Publication financée par une institution

Dates et versions

hal-04222513 , version 1 (29-09-2023)

Identifiants

Citer

Patrice Perrenot, Adrien Fauchier-Magnan, Marta Mirolo, Lauréline Lecarme, Pierre-Henri Jouneau, et al.. Room-Temperature Sintering of Amorphous Thiophosphate Solid Electrolyte (Li 3 PS 4 ): Coupling Morphological Evolution to Electrochemical Properties. Advanced Functional Materials, 2024, 34 (2), ⟨10.1002/adfm.202310739⟩. ⟨hal-04222513⟩
60 Consultations
33 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More