CO 2 methanation over LDH derived NiMgAl and NiMgAlFe oxides: Improving activity at lower temperatures via an ultrasound-assisted preparation - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Chemical Engineering Journal Année : 2023

CO 2 methanation over LDH derived NiMgAl and NiMgAlFe oxides: Improving activity at lower temperatures via an ultrasound-assisted preparation

Josefine Schnee

Résumé

Within the idea to catalyze CO 2 methanation NiMgAl and NiMgAlFe oxides were synthesized by the layered double hydroxide route using co-precipitation and ultrasound-assisted co-precipitation. MgAl and MgAlFe oxides-supported Ni materials prepared by the impregnation method were used as references. Inductively-coupled plasma optical emission spectroscopy, X-ray diffraction, thermal decomposition, H 2-temperature programmed reduction, N 2 physisorption, and transmission electron microscopy were used to characterize the catalysts. NiMgAl prepared using ultrasound-assisted coprecipitation showed the best activity with no deactivation for 40 h under stream. This was attributed mainly to the lower particle size, the higher specific surface area and pore volume as well as the better dispersion of nickel active species at the surface of the concerned materials. In our case, the ultrasound method saves a lot of time during the synthesis process since the maturation phase lasts only 30 min instead of 18 h required for the traditional co-precipitation.
Fichier principal
Vignette du fichier
article CEJ.pdf (1.03 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04212860 , version 1 (20-09-2023)

Identifiants

Citer

Michel Obeid, Christophe Poupin, Madona Labaki, Samer Aouad, Sharad Gupta, et al.. CO 2 methanation over LDH derived NiMgAl and NiMgAlFe oxides: Improving activity at lower temperatures via an ultrasound-assisted preparation. Chemical Engineering Journal, 2023, 474, pp.145460. ⟨10.1016/j.cej.2023.145460⟩. ⟨hal-04212860⟩
51 Consultations
34 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More