Mid-infrared laser operation of (Er0.07La0.10Y0.83)2O3 sesquioxide ceramic - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Laser Physics Letters Année : 2023

Mid-infrared laser operation of (Er0.07La0.10Y0.83)2O3 sesquioxide ceramic

Stanislav Balabanov
  • Fonction : Auteur
Liza Basyrova
  • Fonction : Auteur
Dmitry Permin
  • Fonction : Auteur
Denis Kosyanov
  • Fonction : Auteur
Timofey Evstropov
  • Fonction : Auteur
Sergey Filofeev
  • Fonction : Auteur
Alain Braud
Patrice Camy
  • Fonction : Auteur

Résumé

Abstract A transparent sesquioxide ceramic (Er 0.07 La 0.10 Y 0.83 ) 2 O 3 was fabricated by vacuum sintering at 1780 °C for 3 h with lanthana acting as a sintering additive. It was of single-phase nature (sp. gr. Ia 3 ˉ ) with a close-packed microstructure (average grain size: 17 μ m, pore content: 5 ppmv) and high transparency of 80% at 1.1 μ m. The La 3+ ions induced additional inhomogeneous broadening in the absorption and emission spectra of Er 3+ ions. For the 4 I 11/2 → 4 I 13/2 transition, the stimulated-emission cross-section σ SE was 1.06 × 10 −20 cm 2 at 2719 nm and the luminescence lifetimes of the 4 I 11/2 / 4 I 13/2 states amounted to 2.73/5.91 ms, respectively. A (Er 0.07 La 0.10 Y 0.83 ) 2 O 3 ceramic laser generated 300 mW at 2840 nm with a slope efficiency of 27.7% and a laser threshold of only 17 mW.
Fichier principal
Vignette du fichier
(Er0.07La0.10Y0.83)2O3_sesquioxide_ceramic.pdf (1000.29 Ko) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04211101 , version 1 (01-11-2023)

Identifiants

Citer

Stanislav Balabanov, Pavel Loiko, Liza Basyrova, Dmitry Permin, Denis Kosyanov, et al.. Mid-infrared laser operation of (Er0.07La0.10Y0.83)2O3 sesquioxide ceramic. Laser Physics Letters, 2023, 20 (4), pp.045801. ⟨10.1088/1612-202X/acbce4⟩. ⟨hal-04211101⟩
30 Consultations
47 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More