[(CH3)(2)NH2](2)PdBr4, a layered hybrid halide perovskite semiconductor with improved optical and electrical properties

Résumé

Inspired by the success of three-dimensional hybrid perovskites (CH3NH3)PbX3 (X = Cl, Br, I), two-dimensional (2D) organic-inorganic hybrid metal halides have drawn immense attention due to their highly tunable physical properties. Moreover, although 3D hybrid perovskite materials have been reported, the development of new organic-inorganic hybrid semiconductors is still an area in urgent need of investigation. Here, we used the dimethylammonium cation to construct a palladium-based halide perovskite material [(CH3)(2)NH2](2)PdBr4 with a 2D layered structure. This layered perovskite undergoes one endothermic peak at 415 K corresponding to melting of the organic molecule. The thermal stability of the compound is up to about 500 K. The activation energy and conduction mechanisms are discussed, and the optical study shows a gap energy equal to 2.5 eV. The electrical AC conductivity is in the order of 10(-4) and omega;(-1) cm(-1), which confirms the semiconductor character of this material and indicates its importance in the optoelectronic domain.

Domaines

Chimie
Fichier principal
Vignette du fichier
d3ra04085b.pdf; (1.75 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte

Dates et versions

hal-04193362 , version 1 (01-09-2023)

Licence

Paternité

Identifiants

Citer

Kawther Trabelsi, Nidhal Drissi, Fadhel Hajlaoui, Mustapha Zaghrioui, Abdallah Rhaiem, et al.. [(CH3)(2)NH2](2)PdBr4, a layered hybrid halide perovskite semiconductor with improved optical and electrical properties. RSC Advances, 2023, 13 (33), pp.23348-23358. ⟨10.1039/d3ra04085b⟩. ⟨hal-04193362⟩
30 Consultations
15 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More