Structure-activity relationships in metal organic framework derived mesoporous nitrogen-doped carbon containing atomically dispersed iron sites for CO2 electrochemical reduction - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Catalysis Année : 2019

Structure-activity relationships in metal organic framework derived mesoporous nitrogen-doped carbon containing atomically dispersed iron sites for CO2 electrochemical reduction

Dates et versions

hal-04109576 , version 1 (30-05-2023)

Identifiants

Citer

Xiaohui Sun, Riming Wang, Samy Ould-Chikh, Dmitrii Osadchii, Guanna Li, et al.. Structure-activity relationships in metal organic framework derived mesoporous nitrogen-doped carbon containing atomically dispersed iron sites for CO2 electrochemical reduction. Journal of Catalysis, 2019, 378, pp.320-330. ⟨10.1016/j.jcat.2019.09.013⟩. ⟨hal-04109576⟩