Ultra-low lattice thermal conductivity in tungsten-based scheelite ceramics - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Alloys and Compounds Année : 2023

Ultra-low lattice thermal conductivity in tungsten-based scheelite ceramics

Résumé

BaWO4, Ce2/3□1/3WO4 and La2/3□1/3WO4 polycrystalline ceramics were synthesized by conventional solid-state reaction route. The effect of cation-deficiency on the crystallographic structure, microstructure and thermal properties of these scheelite-type compounds were investigated. X-ray diffraction was used to identify the single-phase scheelite structure of the studied ceramics. Scanning Electron Microscopy technique has revealed a homogenous and dense microstructure with a few micro-cracks. The thermal conductivity of BaWO4 scheelite decreases from 1.3±0.2 to 1.0±0.1 W m-1 K-1 in the range 373 K-673 K. The cation-deficient scheelites Ce2/3□1/3WO4 and La2/3□1/3WO4 ceramics display an ultra-low thermal conductivity of 0.3±0.04 W m-1 K-1 and 0.2±0.03 W m-1 K-1 at 673 K, respectively. These materials exhibit among the lowest known values of thermal conductivity in crystalline oxides, in this temperature range. Therefore, they appear as very attractive for thermal barrier coating and thermoelectric applications.
Fichier principal
Vignette du fichier
Ultra-low_lattice_thermal_conductivity_in_tungsten-based_scheelite_ceramics.pdf (615.29 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Licence : CC BY - Paternité

Dates et versions

hal-04099589 , version 1 (17-05-2023)

Identifiants

Citer

Hicham Ait Laasri, Eliane Bsaibess, Fabian Delorme, Guillaume F. Nataf, Fabien Giovannelli. Ultra-low lattice thermal conductivity in tungsten-based scheelite ceramics. Journal of Alloys and Compounds, 2023, 955, pp.170167. ⟨10.1016/j.jallcom.2023.170167⟩. ⟨hal-04099589⟩
26 Consultations
27 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More