Mechanical tensile behaviour of cement paste/aggregate bond exposed to leaching

Résumé

An experimental program is oriented to the mechanical behaviour of the Interfacial Transition Zone (ITZ) exposed to leaching, for a single mix. Leaching kinetics of the degraded depth, measured through grey level on cross sections, reveals a maximum gap of 10 % between ITZ and bulk cement paste. ITZ, with a main thickness of 15 µm suffers a significant decalcification, which is reflected on the mechanical properties of the bond. Grey level, Calcium/Silicon (Ca/Si) molar ratio and Young’s modulus in the degraded zone present similar evolution. Effect of ITZ causing cracking and then debonding is noticed, through chemical analysis, image observation and mechanical tests.
Fichier non déposé

Dates et versions

hal-04071077 , version 1 (17-04-2023)

Identifiants

Citer

Andrei Gîrboveanu, Mouad Jebli, Frédéric Jamin, Vincent Huon, Laurent Bonnet, et al.. Mechanical tensile behaviour of cement paste/aggregate bond exposed to leaching. Construction and Building Materials, 2023, 369, pp.130592. ⟨10.1016/j.conbuildmat.2023.130592⟩. ⟨hal-04071077⟩
43 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More