High-Entropy FeCoNiB0.5Si0.5 Alloy Synthesized by Mechanical Alloying and Spark Plasma Sintering

Résumé

A FeCoNi(B0.5Si0.5) high-entropy alloy with the face-centered cubic (FCC) crystal structure was synthesized by mechanical alloying and spark plasma sintering (SPS). Phase evolution, microstructure, morphology and annealing behaviors were investigated. It was found that a single FCC solid solution appears after 50 h of milling. The grain size was 10 nm after 150 h of milling. Microstructure parameters were calculated by the Rietveld fitting of the X-ray Diffraction patterns. Magnetic characterizations of milled and annealed powders at 650 °C for 1 h were investigated. The heat treatment improves the magnetic properties of the milled powders by enhancing the saturation magnetization value from 94.31 to 127.30 emu/g and decreasing the coercivity from 49.07 to 29.57 Oe. The cohabitation of the FCC phase with the equilibrium crystalline phases observed after annealing is responsible of this magnetic softening. The as-milled powder was also consolidated by spark plasma sintering at 750 and 1000 °C. The obtained specimen consolidated at 750 °C improved the coercivity to 25.06 Oe and exhibited a compressive strength of 1062 Mpa and Vickers hardness of 518 ± 14 HV, with a load of 2 kN. The nanoindentation technique with the Berkovich indentor gave hardness and indentation elastic modulus of 6.3 ± 0.3 Gpa (~640 HV) and 111 ± 4 Gpa for samples consolidated by SPS at 750 °C.

Domaines

Matériaux
Fichier principal
Vignette du fichier
crystals 2020 - High Entropy FeCoNiB0.5Si0.5.pdf (1.91 Mo) Télécharger le fichier
Origine Publication financée par une institution

Dates et versions

hal-04012362 , version 1 (02-03-2023)

Identifiants

Citer

Zaara Kaouther, Mahmoud Chemingui, Sophie Le Gallet, Yves Gaillard, Lluisa Escoda, et al.. High-Entropy FeCoNiB0.5Si0.5 Alloy Synthesized by Mechanical Alloying and Spark Plasma Sintering. Crystals, 2020, 10 (10), pp.929. ⟨10.3390/cryst10100929⟩. ⟨hal-04012362⟩
20 Consultations
21 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More