EBSD, XRD and SRS characterization of a casting Al-7wt%Si alloy processed by equal channel angular extrusion: Dislocation density evaluation - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Materials Characterization Année : 2019

EBSD, XRD and SRS characterization of a casting Al-7wt%Si alloy processed by equal channel angular extrusion: Dislocation density evaluation

Résumé

Aluminum-silicon (AleSi) alloys of high silicon contents are composite materials; they are used whenever high casting properties are required. They are slightly ductile below 8wt%Si. An increase in ductility can be obtained by refining Si-crystals in elaboration or by a further hot working. In the present work, an Al-7wt%Si alloy was processed by Equal Channel Angular Extrusion (ECAE) at temperatures 20 °C and 160 °C up to three passes. The die was formed by two cylindrical channels with characteristic angles Φ = 110°and Ψ = 0. EBSD, X ray diffraction (XRD) and Strain Rate Sensitivity (SRS) were used to characterize the microstructure and the mechanical properties. High levels of strain were introduced at both temperatures. The activation volume was lowered to 125b 3 and 210b 3 at 20 °C and 160 °C respectively and was considered to be dislocation density dependent. The remaining dislocation densities calculated from EBSD, XRD and SRS experiments are quite different. This was explained by the scale difference and by the sensitivities of the methods to the free surface effect.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Text and figures for HAL.pdf (1.2 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-04012357 , version 1 (02-03-2023)

Identifiants

Citer

Zahra Zribi, Hassan Houcin Ktari, Frédéric Herbst, Virgil Optasanu, Nabil Njah. EBSD, XRD and SRS characterization of a casting Al-7wt%Si alloy processed by equal channel angular extrusion: Dislocation density evaluation. Materials Characterization, 2019, 153, pp.190 - 198. ⟨10.1016/j.matchar.2019.04.044⟩. ⟨hal-04012357⟩
13 Consultations
247 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More