High temperature thermoelectric properties of the type-I clathrate Ba8AuxSi46-x

Résumé

The thermoelectric properties of the type-I clathrate Ba8AuxSi46-x (4.10 <= x <= 6.10) were characterized from 300 to 700K. Increasing the Au concentration leads to a transition from an n-type (x < 5.43) to a p-type (x > 5.43) electrical conduction. The experimental data are well described by a single-parabolic-band model assuming a single scattering mechanism of the charge carriers in this temperature range. The lattice thermal conductivity, inferred from degeneracy-adjusted Lorenz numbers, is low regardless of the composition. However, the measured values are significantly lower in the p-type samples possibly due to a combination of a higher degree of disorder in the crystal structure at high Au contents and an enhanced phonon-charge carrier coupling. Even though high thermopower values are achieved, the high electrical resistivity remains the main obstacle to push the dimensionless figure of merit ZT (0.2 at around 600 K for x = 5 .59) beyond the level of the best Si-based clathrate compounds.

Fichier principal
Vignette du fichier
JApplPhys 111, 043706 (2012).pdf (1.32 Mo) Télécharger le fichier
Origine Fichiers éditeurs autorisés sur une archive ouverte
Licence

Dates et versions

hal-03997305 , version 1 (20-02-2023)

Licence

Identifiants

Citer

Christophe Candolfi, Umut Aydemir, Michael Baitinger, Niels Oeschler, Franck Steglich, et al.. High temperature thermoelectric properties of the type-I clathrate Ba8AuxSi46-x. Journal of Applied Physics, 2012, 111 (4), pp.043706. ⟨10.1063/1.3682585⟩. ⟨hal-03997305⟩
38 Consultations
106 Téléchargements

Altmetric

Partager

  • More