Structural, spectroscopic, luminescence and magnetic properties of a novel far-red emitting phosphor Er, Mn doped ZrTe3O8

Résumé

Polycrystalline ZrTe3O8:2%Er, 3%Mn was prepared by the solid-state reaction technique. The formation of single-phase material was determined by X-ray diffraction studies and found to be a cubic phase at room temperature. The structure can be described by two types of polyhedrons, namely disphonoids (TeO4E with E = electronic lone pair of Te4+) and octahedrons of ZrO6. The bridges Te-O1-Te and Te-O2-Zr ensured the crystal structure cohesion. Both kinds of polyhedron oxygen were coordinated along the [0 1 0] mixed chain, linked to a pure chain of tellurium through O1 in order to form a two-dimensional network and then a unit cell with a three-dimensional network. The Raman spectrum was dominated by a strong band at 841 cm-1corresponding to Te-O2-Zr bridges asymmetric stretching vibration. Consequently, the Te-O2 and Zr (Mn)single bondO2 bonds are chemically inequivalent and the Zrsingle bondO2single bondTe bridges are chemically asymmetric. The magnetic results reveal the appearance of a weak ferromagnetic behavior at low temperature.The emission properties of the ZrTe3O8:2%Er, 3%Mn prepared at relatively high temperature examined at 490 nm excitation led to an appearance of an important emission in the visible and near-infrared domains due to homogeneously occupied Er3+ ions in the host lattice. Therefore, this kind of phosphors may be a meaningful reference for W-LEDs application.

Fichier principal
Vignette du fichier
2-Inorg Chem Comm. (S. Kabadou) 2022.pdf (5.8 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Licence

Dates et versions

hal-03983767 , version 1 (04-05-2024)

Licence

Identifiants

Citer

S. Kabadou, J. Horcheni, F. Mselmi, A. Kabadou, E. Dhahri, et al.. Structural, spectroscopic, luminescence and magnetic properties of a novel far-red emitting phosphor Er, Mn doped ZrTe3O8. Inorganic Chemistry Communications, 2022, 140, pp.109429. ⟨10.1016/j.inoche.2022.109429⟩. ⟨hal-03983767⟩
61 Consultations
116 Téléchargements

Altmetric

Partager

  • More