Preparation and characterization of 2D SiC/SiC composites with composition-graded C(B) interphase

Résumé

2D SiC/C(B)/SiC composites were prepared by CVI. The C(B) interphase is made of five successive C(B) layers with increasing boron content from the fibre to the matrix. This composition-graded interphase leads to good mechanical properties similar to those obtained with pure pyrocarbon interphase. However, the lifetime in air under load at high temperature of 2D SiC/C(B)/SiC composites is not improved despite the high percentage of boron in several sublayers of the interphase. By TEM characterization, the boron-rich layers were found to exhibit a nano-porous texture probably due to a bad control of the growth process within the fibrous preforms. This nanoporous texture might be responsible for the poor oxidation resistance of these sublayers and consequently the rather short lifetime of the real 2D composites with respect to those previously reported for 1D SiC/C(B)/SiC model microcomposites.

Domaines

Chimie
Fichier principal
Vignette du fichier
Preprint - 2D SiC-SiC with C(B) CGI - JECS 1997.pdf (4.93 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03967016 , version 1 (01-02-2023)

Identifiants

Citer

Sylvain Jacques, A. Guette, F. Langlais, R. Naslain, S. Goujard. Preparation and characterization of 2D SiC/SiC composites with composition-graded C(B) interphase. Journal of the European Ceramic Society, 1997, 17 (9), pp.1083-1092. ⟨10.1016/S0955-2219(96)00216-6⟩. ⟨hal-03967016⟩

Collections

CEA CNRS DAM
11 Consultations
26 Téléchargements

Altmetric

Partager

More