Soft polymerization of hexamethyldisiloxane by coupling pulsed direct‐liquid injections with dielectric barrier discharge - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Plasma Processes and Polymers Année : 2023

Soft polymerization of hexamethyldisiloxane by coupling pulsed direct‐liquid injections with dielectric barrier discharge

Résumé

This work examines the combination of pulsed direct-liquid injections with dielectric barrier discharge at atmospheric pressure for the deposition of organosilicon coatings using hexamethyldisiloxane (HMDSO) as the precursor and nitrogen as the carrier gas. In such conditions, deposition relies on the charging of micrometer droplets and their transport toward the substrate by the Coulomb force. The thin-film morphology and extent of precursor fragmentation are strongly linked to the amount of energy provided by the filamentary discharge to HMDSO droplets. While cross-linked and smooth coatings were achieved at low energies as in standard gas phase plasma polymers, viscous and droplet-like structured thin films were deposited at higher energies. The latter material is attributed to the soft polymerization of HMDSO droplets related to plasma–droplet interactions.
Fichier principal
Vignette du fichier
Cacot, Soft polymerization of hexamethyldisiloxane, 2023.pdf (5.45 Mo) Télécharger le fichier
Origine Publication financée par une institution

Dates et versions

hal-03920019 , version 1 (16-02-2023)

Licence

Identifiants

Citer

Laura Cacot, Guillaume Carnide, Myrtil L Kahn, Nicolas Naudé, Luc Stafford, et al.. Soft polymerization of hexamethyldisiloxane by coupling pulsed direct‐liquid injections with dielectric barrier discharge. Plasma Processes and Polymers, 2023, 20 (3), pp.e2200165. ⟨10.1002/ppap.202200165⟩. ⟨hal-03920019⟩
43 Consultations
40 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More