Anisotropic fracture in nacre-like alumina

Résumé

Fracture in nacre-like alumina is studied experimentally and numerically with alumina platelets main alignment direction perpendicular (along-configuration) to the one commonly tested (acrossconfiguration) in the literature. In along-configuration, brittle failure is noted after crack initiation with no macroscopic crack deviation, unlike what is observed in across-configuration. However, NLA exhibits in along configuration initiation critical stress intensity factor KIc = 5.3 ± 0.5 MPa.m1/2, in the same order of magnitude as in across-configuration. The increase in KIc compared to monolithic alumina can be explained by a phenomenon of crack initiation containment at the interface between platelets. Unstable crack propagation occurs just after initiation, mainly following the platelet interfaces which results in crenelated fracture surfaces with crack decentering with respect to the initial notch tip
Fichier principal
Vignette du fichier
Anisotropic_fracture_nacre_like_alumina.pdf (4.76 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Licence : CC BY - Paternité

Dates et versions

hal-03885621 , version 1 (06-12-2022)
hal-03885621 , version 2 (12-05-2023)

Identifiants

Citer

Thomas Duminy, Ronan Henry, Jérôme Adrien, Aurélien Doitrand, Sylvain Meille. Anisotropic fracture in nacre-like alumina. Theoretical and Applied Fracture Mechanics, 2023, 123, pp.103710. ⟨10.1016/j.tafmec.2022.103710⟩. ⟨hal-03885621v2⟩
51 Consultations
30 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More