α-tricalcium phosphate synthesis from amorphous calcium phosphate: structural characterization and hydraulic reactivity

Résumé

In the present study, amorphous tricalcium phosphate (TCP) has been synthetized by a wet route to obtain low temperature α-TCP at 650 °C (LT-αTCP) and compare its structural, physical–chemical and thermal properties with those of α-TCP obtained by the conventional solid-state reaction method at 1400 °C (HT-αTCP). Even if no significant differences were observed concerning the values of lattice parameters measured by Rietveld refinement, LT-αTCP presented lower crystallinity and higher crystal strains than HT-αTCP. The reactivity in water of the α-TCP obtained by the two different routes was assessed. Both raw samples appeared relatively inert in solution and did not favour the nucleation of calcium deficient apatite (CDA); the LT-αTCP and HT-αTCP were converted into apatite only after milling. The mechanical process leads to a decrease in crystallinity and the formation of an amorphous phase, which is supported in this work by Raman spectroscopy. The faster rate of conversion of milled LT-αTCP compared to HT-αTCP can be assigned to its higher specific surface area, lower crystallinity and higher residual crystal strain; these favour the dissolution of the α-TCP phase. Finally, the setting properties of α-TCP-based bone cements were compared regarding their synthesis route. Although the synthesis route does not significantly affect the setting times, the kinetic of conversion into CDA was faster for LT-αTCP than for HT-αTCP. Thus, the modulation of the dissolution rate of α-TCP-based cement determined by the preparation route and the grinding process allows control of the overall setting reaction.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Martinez_2021.pdf (1.75 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03871420 , version 1 (31-05-2023)

Identifiants

Citer

T. Martinez, M. Espanol, Cédric Charvillat, Olivier Marsan, M. Ginebra, et al.. α-tricalcium phosphate synthesis from amorphous calcium phosphate: structural characterization and hydraulic reactivity. Journal of Materials Science, 2021, 56 (24), pp.13509-13523. ⟨10.1007/S10853-021-06161-0⟩. ⟨hal-03871420⟩
24 Consultations
110 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More