Tm,Ho:Ca(Gd,Lu)AlO4 crystals: Crystal growth, structure refinement and Judd-Ofelt analysis
Résumé
Mixed” calcium rare-earth aluminate laser host crystals Ca(Gd,Lu)AlO4 (CALGLO) with up to 10.8 at.% Lu codoped with Tm3+ and Ho3+ ions are grown by the Czochralski method along the [001] direction. The segregation of rare-earth ions is studied. The crystal structure is refined by the Rietveld method. Tm,Ho:Ca(Gd,Lu)AlO4 crystallizes in the tetragonal system (sp. gr. I4/mmm) exhibiting a K2NiF4 type structure. The lattice constants are a = 3.6585(6) Å and c = 11.9660(9) Å for a crystal with a composition of CaGd0.8947Lu0.0551Tm0.0448Ho0.0054AlO4. The stability of Ca(Gd,Lu)AlO4 solid-solutions is discussed. The polarized Raman spectra are measured, revealing a most intense mode at 311 cm−1 and a maximum phonon frequency of ∼650 cm−1. The polarized absorption spectra are measured. The transition intensities for the Ho3+ ion are analyzed using the modified Judd-Ofelt theory accounting for configuration interaction.
Domaines
Optique [physics.optics]
Fichier principal
JALCOM_Mixed_TmHoCALGO_crystal_Part_I_ready_for_submission.pdf (1.05 Mo)
Télécharger le fichier
Origine | Fichiers produits par l'(les) auteur(s) |
---|